Casting Manufacturing

Casting Manufacture :-

Casting is an engineering manufacturing process generally used for mass production in which materials in a molten state are poured into a mould where they solidify. In this process, complex parts can be manufactured economically and rapidly that otherwise would involve a lot of time if produced by other methods like shaping or cutting. Casting process can be utilized to produce a large variety of parts that are used in different industries, ranging from a small plastic toy to a large gas turbine blade.

Wide Range Of Casting Services

 

Hi Tech Enterprises is capable for production of different types of materials such as :

·         Cast Iron(CI) Castings

·         Ni Hard Castings

·         Manganese Steel Castings

·         Aluminium Castings, etc.

Additional Information:

• Minimum Order Quantity: 5 Piece

Ni Hard CastingsManufacturer & Exporter of Ni Hard Castings.

We offer our client an excellent quality range of Ni-Hard Castings, which are manufactured from high grade quality raw materials. These NiI-Hard Castings can be customized as per our valued customers specifications. These Ni-Hard Castings are widely known for its durability and quality. We manufacture all types of Ni-Hard Casting Grade 1, 2 & 4.

Ni-Hard is the generic name for a family of white cast irons alloyed with nickel and chromium to give high hardness and outstanding resistance to abrasion.

Ni-Hard is an extremely wear resistant material and in cast form is ideal for use with abrasive products, giving a much more extended life when compared with cast iron or mild steel when incorporated in pneumatic conveying systems.

Nickel content increases with section size or cooling time of the casting to inhibit pearlitic transformation. For castings of 38 mm to 50 mm thick, 3.4% to 4.2% Ni is sufficient to suppress pearlite formation upon mold cooling. Heavier sections may require nickel levels up to 5.5% to avoid the formation of pearlite. It is important to limit nickel content to the level needed for control of pearlite; excess nickel increases the amount of retained austenite and lowers hardness.

There are two distinct groups of Ni-Hard compositions:
• The medium alloyed Ni-Hard 1 and Ni-Hard 2.
• Ni-Hard 4.

These alloys are standardized in almost all industrialized nations under various designations.

With an exceptional talent of our competent team, we are offering our valued clients a wide series of cast iron casting that is manufactured as per international quality standards. We are among the reputed names in the industry for manufacturing Iron Casting. The offered product is used in casting and foundry industries for automating machinery and increasing the productivity. It helps in the efficient planning and scheduling of production tasks and is cost effective as well.

Features:

• Excess feasiblity and durablity
• Better performance
• Good in result